涂料缺陷（Paint Defects）
邊角失效（EDGE BREAKDOWN）
1．描述（Description）:
一種涂層失效，通常以結構邊角腐蝕或涂層撕裂的形式出現?？赡馨l生在任何尖銳邊緣的區域，如焊縫等，邊角失效如圖1所示。Coating failure, usually in the form of corrosion or tearing to edges of a structure. Can also happen to any areas of sharp edges such as welds etc. 圖1 邊角失效圖
2．可能原因（Probable Causes）:
通常由于漆膜厚度不足和/或沒有做預涂；鋼表面沒有做任何的預處理如做一個2mm的倒角。Usually inadequate paint film thickness and/or lack of stripe coats(s). Steel surface may not have any pre-treatment such as a radius of the recommended 2mm.
3．預防措施（Prevention）:
為所有邊角做倒角處理；修整焊縫和凸起部位；提前做好預涂或在整體噴涂后補涂一層油漆。Radius all edges where possible. Dress welds and protrusions. Apply brush/stripe coats at the appropriate time to suit coating system. This may be prior to full coat or after full coat.
4．修復方法（Repair）:
取決于涂層破裂的程度。必要時進行局部修補，對現有涂層進行拉毛處理和現場修補；檢查涂層之間的兼容性；必要時修整鋼結構。Depends upon extent of coating breakdown. Conduct localised repair where necessary, feather edge existing coating and spot repair. Check compatibility between coats. Dress steelwork as necessary.
5．專業名詞解析（Interpretation of professional terms）:
涂層在固化過程中，溶劑的揮發以及進一步的交聯反應等因素會使涂層體積收縮而形成內應力，如內應力積累至大于內聚力，涂層便會撕裂。這在邊角處會顯得尤為明顯，邊角處承受來自于兩邊涂層的內應力拉力，同時邊角處通常具有更薄的涂層厚度，尖銳的邊角也會像一把刀一樣對涂層形成剪切力，因此倒角處非常容易失效，這就是我們常說的“邊角效應”，邊角效應原理圖如圖2所示。
圖2 邊角效應原理圖
倒角即將尖銳的邊角通過打磨、切削等手段進行倒圓處理，從而減少應力的集中。如規格書要求滿足ISO 8501-3中P3等級的要求，則必須進行倒角處理，不同部位的倒角方式示意圖如圖3所示。
圖3 不同部位的倒角方式示意圖
注：本站系本網編輯轉載，轉載目的在于傳遞更多信息，并不代表本網贊同其觀點和對其真實性負責。如涉及作品內容、版權和其它問題，請在30日內與本網聯系，我們將在第一時間刪除內容！[聲明]本站文章版權歸原作者所有 內容為作者個人觀點 本站只提供參考并不構成任何投資及應用建議。本站擁有對此聲明的最終解釋權